Aluminium Alloy 1200 O Foil
1200 is industrial pure aluminum, with high plasticity, corrosion resistance, conductivity and other properties, but low strength, heat treatment can not be strengthened, workability; welding, hydrogen atom welding and contact, not easy to weld; easy to cause various pressure processing and extension ,bending.
Glacier: heating temperature 350～410℃; heating temperature 350～410℃; air circulation time between 30～120min, depending on the effective thickness of the material; or water cooling. 2) High temperature flame: heating temperature 350～500℃; when the thickness of the finished product is ≥6mm, the time is 10～30min, when it is less than 6mm, heat will pass through; air cooling. 3) Low temperature flame heating temperature 150～250℃; blood drawing time 2～3h; air cooling and water cooling.
200 callback is a kind of high-strength hard aluminum, which belongs to the Al-Cu-Mg series alloy. Mainly used to make various high-load parts. It can be heat treated to strengthen, quenching and just quenching plastic deformation strength.
This is a high-strength aluminum material that can be strengthened by heat treatment, plastic strength in quenched and freshly quenched states, and cold strength during spot welding and gas welding. The alloy can be a chemical material after quenching and hardening. The performance is acceptable, but the chemical resistance after flame is low: or the resistance is not high. Generally, lead treatment and aluminum-coated surface are used to improve its anti-corrosion ability. Mainly used to make various high-load parts. And (but not including accessory forgings) such as aircraft parts, skins, bulkheads, wing ribs, spars, nails and other working parts below 150°C. Aluminum alloy is the most widely used non-ferrous metal structural material in industry, and it has been widely used in aviation, aerospace, automobile, machinery manufacturing, shipbuilding and chemical industries.
Raw Materials Of Aluminum Foil 8079 HO 8 Micrones For Food Wrapping It is a kind of aluminum foil with high strength, good elongation and compression properties